Unitized split seal for bearing and gearbox protection
Product Advantages
- Split design eliminates the need for equipment disassembly
- New design and materials proven to outperform conventional lip seals
- Patented design combines high performance PTFE and polymer materials
- Filled PTFE materials provide high wear and abrasion resistance
Product Characteristics Parameters
| Specifications | ||||||
| Material (adapters/sealer rings) | Size Range* mm (inch) | Temperature ˚C (˚F) | Speed m/s (ft/min) | Pressure MPa (psi) | Recommended use | Mating surface (Rockwell C) |
| AWC800 Adapters (EU) | ||||||
| AWC100 (PTFE) Polyimide |
25 ─ 610 (1 ─ 24) |
85 (185) |
12.7 (2500) |
0.007 (1) |
Excellent dry Excellent low viscosity |
≥45 |
| AWC300 (PTFE) Molybdenum & glass |
25 ─ 610 (1 ─ 24) |
85 (185) |
12.7 (2500) |
0.007 (1) |
Excellent high viscosity Good dry and good in water |
≥55 |
| AWC400 (PTFE) Carbon & graphite |
25 ─ 610 (1 ─ 24) |
85 (185) |
12.7 2500 |
0.007 (1) |
Excellent in water Good dry and low viscosity |
≥55 |
| AWC860 Adapters (EU) | ||||||
| AWC100 (PTFE) Polyimide |
25 ─ 457 (1 ─ 18) |
121 (250) |
12.7 2500 |
0.007 (1) |
Excellent dry Excellent low viscosity |
≥45 |
| AWC300 (PTFE) Molybdenum & glass |
25 ─ 457 (1 ─ 18) |
121 (250) |
12.7 2500 |
0.007 (1) |
Excellent high viscosity Good dry and good in water |
≥55 |
| AWC400 (PTFE) Carbon & graphite |
25 ─ 457 (1 ─ 18) |
121 (250) |
12.7 2500 |
0.007 (1) |
Excellent in water Good dry and low viscosity |
≥55 |
| Performance depends on concurrent conditions including shaft hardness, shaft surface roughness, material, lubrication, temperature, and pressure. | ||||||
| Applicable standards: ISO3760/ISO3761 | ||||||
| *Please contact your Chesterton representative for larger sizes | ||||||